China 4j36 Invar Alloy Wire Low Expansion Alloy Feni36 Wire Manufacture and Factory |TANKII

4j36 Invar Alloy Wire Low Expansion Alloy Feni36 Wire Featured Image

4j36 Invar Alloy Wire Yakaderera Kuwedzera Alloy Feni36 Wire

Tsanangudzo Pfupi:

DIN 17745 4j36 Invar Alloy Wire Low Expansion Alloy Feni36 Wire

(Zita rakajairika: Invar, FeNi36, Invar Standard, Vacodil36)

4J36 (Invar), inozivikanwawo seFeNi36 (64FeNi muUS), iine nickel-iron alloy inozivikanwa neiyo yakasarudzika yakaderera coefficient yekuwedzera kwekupisa (CTE kana α).

Muenzaniso NO.:Invar

OEM:Ehe

Nyika:Yakapfava 1/2 yakaoma yakaoma T-yakaoma

HS Kodhi:74099000

KwakabvaChina

Density:8.1

Tumira email kwatiri

Product Detail

FAQ

Product Tags

4J36 (Invar) inoshandiswa panodiwa kugadzikana kwepamusoro-soro, senge zviridzwa, wachi, seismic creep gauges, terevhizheni shadow-mask mafuremu, mavharuvhu mumamotor, uye antimagnetic wachi.Mukuongorora ivhu, kana yekutanga-odha (yakakwirira-chaiyo) kukwirisa kukwirisa kunofanirwa kuitwa, vashandi veLevel (leveling rod) inoshandiswa inogadzirwaInvar, panzvimbo pehuni, fiberglass, kana mamwe simbi.Invar struts yakashandiswa mune mamwe mapistoni kudzikamisa kuwedzera kwavo kupisa mukati memasilinda avo.

4J36 shandisa oxyacetylene welding, magetsi arc welding, welding uye dzimwe nzira dzekugadzira.Sezvo coefficient yekuwedzera uye kuumbwa kwemakemikari ealloy kwakabatana kunofanirwa kudzivirirwa nekuda kwewelding kukonzeresa shanduko mune alloy kuumbwa, zviri nani kushandisa Argon arc welding welding filler simbi zvine 0.5% kusvika 1.5% titanium, kuitira kuderedza weld porosity uye kuputika.

Zvakajairwa

Ni	35~37.0	Fe	Bal.	Co	-	Si	≤0.3
Mo	-	Cu	-	Cr	-	Mn	0.2~0.6
C	≤0.05	P	≤0.02	S	≤0.02

Coefficient yekuwedzera

θ/ºC	α1/10-6ºC-1	θ/ºC	α1/10-6ºC-1
20~-60	1.8	20~250	3.6
20~-40	1.8	20~300	5.2
20~-20	1.6	20~350	6.5
20~-0	1.6	20~400	7.8
20~50	1.1	20~450	8.9
20~100	1.4	20~500	9.7
20~150	1.9	20~550	10.4
20-200	2.5	20~600	11.0

Typical Physical properties

Density (g/cm3)	8.1
Electrical resistivity pa20ºC(OMmm2/m)	0.78
Tembiricha yekudzivirira (20ºC~200ºC)X10-6/ºC	3.7~3.9
Thermal conductivity, λ/ W/(m*ºC)	11
Curie point Tc/ ºC	230
Elastic Modulus, E/Gpa	144

Nzira yekurapa kupisa
Annealing yekubvisa stress	Kupisa kusvika 530 ~ 550ºC uye kubata 1 ~ 2 h.Kutonhora pasi
annealing	Kuti ubvise kuomarara, izvo zvinoburitsa muinotonhora-yakakungurutswa, inotonhora yekudhirowa.Anealing inoda kudziyisa kusvika 830 ~ 880ºC muvacuum, bata 30 min.
The stabilization process	Mune inodzivirira midhiya uye inopisa kusvika 830 ºC, bata 20min.~ 1h, kudzima Nekuda kwekushushikana kunoitwa nekudzima, kudziyisa kusvika 315ºC, bata 1 ~ 4h.
Zvekungwaririra	Haikwanise kuomeswa nekurapwa kwekupisa Kurapa kwepamusoro kunogona kuita jecha, kupukuta kana kunhonga. Alloy inogona kushandiswa 25% hydrochloric acid pickling solution pa70 ºC kubvisa nzvimbo ine oxidized.