FeCrAl 0cr23al5 yekudziya element flat waya & strip nefekitori
FeCrAl 0cr23al5 kupisa chinhu furati waya &stripnefekitari
| Giredhi | 0Cr23Al5 |
| Size | ukobvu: 0.05-3mm upamhi: 4-250mm |
| Surface | kutsemuka kwakajeka |
| Kurema | 1-3kg/roll, zvichienderana nehuwandu hwevatengi |
| Resistivity | 1.3±0.05μΩ.m |
| Kuoma (HV) | 180-210HV |
| Elongation | ≥16% |
| Giredhi | Kupisa kwakanyanya | Resistivity | Kuoma | Kusimba simba | Elongation |
| 0Cr13Al4 | 1050 ℃ | 1.25±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300 ℃ | 1.42±0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150 ℃ | 1.12±0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100 ℃ | 1.04±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20(310S) | 1100 ℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Giredhi | Kemikari yakagadzirwa% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | ＜1 | 4.8-5.0 | balance |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | balance |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | ＜1 | 4.8-5.0 | balance |
| Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | balance | ＜0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | ＜0.5 | balance |
| Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | balance |
| Cr25Ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | balance |
Shanghai Tankii Alloy Material Co., Ltd. tarisa pakugadzirwa kwenichrome alloy, thermocouple wire, fecral alloy, precision alloy, copper nickel alloy, thermal spray alloy nezvimwewo nenzira yewaya, shiti, tepi, tambo, tsvimbo uye ndiro.
Takatowana ISO 9001 quality system certificate uye kubvumirwa kwe ISO 14001 Environmental Protection System.Tine seti yakakwana yekugadzirwa kwepamusoro kwekunatsa, kuderedza kutonhora, kudhirowa uye kupisa kupisa nezvimwewo. Isu tinozvikudzawo tine R&D yakazvimirira.
Nyora meseji yako pano ugotitumira