China Constantan Flat Wire Copper Nickel Alloy 6j40 Ribhoni 0.4*2mm Kugadzira uye Fekitori

Constantan Flat Wire Copper Nickel Alloy 6j40 Ribhoni 0.4*2mm

Tsananguro pfupi:

Constantan Flat Wire Copper Nickel Alloy 6j11 Ribhoni 0.4*2mm

Resistivity ( 200C μ Ω . m): 0.1
Kupisa kwakanyanya kushanda (0C): 200
Simba reKusimba (Mpa): ≥ 250
Nzvimbo yekunyunguduka (0C): 1095
Kuwanda (g/cm3):8.9
TCR x10-6/ 0C (20~600 0C): < 100

Chitupa:ISO 9001

Saizi:Yakagadzirirwa

zita rechigadzirwa:Nickel Alloy yemhangura 6j11

kushandiswa:indasitiri

zvinhu:chiwanikwa

chinhu:kuramba kwakanyanya

basa:kugadzikana kwakanaka kwechimiro

huremu:zvakavakirwa pa

chiyero:sezvinodiwa nemutengi

ruvara:bhurawuni

chimiro:waya

MOQ: (Zvinyorwa zveMOQ):20kg

Tumira email kwatiri

Ruzivo rweChigadzirwa

Mibvunzo Inowanzo bvunzwa

Matagi eChigadzirwa

Itsva Constantan Flat Wire Copper Nickel Alloy 6j11 Ribhoni 0.4*2mm

Hunhu	Kuramba (200C μΩ.m)	Tembiricha yepamusoro inoshanda (0C)	Simba reKusimba (Mpa)	Nzvimbo yekunyunguduka (0C)	Kuwanda (g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Mazita eAlloy
NC003 (CuNi1)	0.1	200	≥ 250	1095	8.9	< 100	-12

Zvimiro zvemuviri	Chiyero	Mhinduro
Kuwanda kwevanhu	8.94 g/cc
Zvivakwa zveMichina	Chiyero	Mhinduro
Simba Rokusimba, Rakakosha	262 – 531 MPa
Simba reKusimba, Kubudirira	276 – 524 MPa	Zvichienderana nehasha
Kureba paKuzorora	46.0%	mu 50.8 mm.
Modulus yeElasticity	115 GPa
Chiyero chePoissons	0.310	Zvaverengerwa
Kugona kuchinjika	20%	UNS C36000 (brass inocheka yakasununguka) = 100%
Shear Modulus	44.0 GPa
Zvivakwa zveMagetsi	Chiyero	Mhinduro
Kuramba kweMagetsi	0.0000120 ohm-cm @Tembiricha 20.0 ° C
Zvivakwa zvekupisa	Chiyero	Mhinduro
CTE, yakatsetseka	17.5 µ m/m-° C @Tembiricha 20.0 – 300 ° C
Kugona Kupisa Kwakakwana	0.380 J/g-° C
Kufambisa kwekupisa	64.0 W/mK @Tembiricha 20.0 ° C
Nzvimbo Yokunyunguduka	< = 1125 ° C	Liquidus
Liquidus	1125 ° C
Zvivakwa zvekugadzirisa	Chiyero	Mhinduro
Kupisa kweAnnealing	565 – 815 ° C
Kupisa Kunoshanda	815 – 950 ° C
Zvimiro zveZvinhu Zvine Chikamu	Chiyero	Mhinduro
Mhangura, Cu	> = 91.2%
Simbi, Fe	1.30 – 1.70 %
Mutungamiriri, Pb	< = 0.050 %
Manganese, Mn	0.30 – 0.80 %
Nickel, Ni	4.80 – 6.20%
Zinc, Zn	< = 1.0 %

Zviri Mukati meCuNi44 Chemical, %

Ni	Mn	Fe	Si	Cu	Zvimwe	Mutemo weROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	Bhari	-	ND	ND	ND	ND

Zvivakwa zveMichina

Tembiricha Yebasa Rinoenderera Mberi Yakanyanya	400ºC
Kusimba kwemuviri pa20ºC	0.49±5%ohm mm2/m
Kuwanda kwevanhu	8.9 g/cm3
Kufambisa kwekupisa	-6 (Max)
Nzvimbo Yokunyunguduka	1280ºC
Simba reKusimba, N/mm2 Yakanamirwa, Yakapfava	340~535 Mpa
Simba reKusimba, N/mm3 Yakakungurutswa nechando	680~1070 Mpa
Kureba (anneal)	25% (Mini)
Kureba (kunotonhora kwakamonerwa)	≥Min)2% (Min)
EMF vs Cu, μV/ºC (0~100ºC)	-43
Maumbirwo eMicrographic	austenite
Pfuma yeMagineti	Kwete